RED. Tee
Socket Welding Type Reducing Tee For Cu-Ni Pipe

■ Material : EEMUA 146 7060X
Unit: mm
Pipe Dimension Remark
N/D O/D D D1 D2 L L1 L2
3/4"X1/2" 25X16 32 25.1 16.1 26.0 13.0 10.0  
1"X3/4" 30X25 37 30.1 25.1 28.5 13.0 13.0  
1"X1/2" 30X16 37 30.1 16.1 28.5 13.0 10.0  
1 1/2"X1" 44.5X30 52 44.6 30.1 41.0 13.0 13.0  
1 1/2"X3/4" 44.5X25 37.0 44.6 25.1 41.0 13.0 13.0  
1 1/2"X1/2" 44.5X16 52.0 44.6 16.1 41.0 13.0 10.0  
*NOTE :
1. Dimension Per EEMUA 146
2. Process : Hot Forming
3. Heat Treatment : Annealing After Hot Forming
4. Temp & Hold Time : 750℃±50℃, 30Min / Inch(THK)
 
3000# Socket Welding Type Reducing Tee For Cu-Ni Pipe

■ Material : ASTM UNS C70600
Unit: mm
Pipe Dimension Remark
N/D D±0.2 D1 C d±0.2 d1 C1 L L1
(MIN.)
2
(MIN.)
AVG. MIN. AVG. MIN.
3/4"X1/2" 20.7 20.7 4.90 4.27 22.0 15.3 4.67 4.09 31.5 12.5 9.5  
1"X1/2" 34.1 26.4 5.69 4.98 22.0 15.3 4.67 4.09 35.0 12.5 9.5  
1"X3/4" 34.1 26.4 5.69 4.98 27.4 20.7 4.90 4.27 35.0 12.5 12.5  
1 1/2"X1/2" 49.0 40.3 6.35 5.54 22.0 15.3 4.67 4.09 44.5 12.5 9.5  
1 1/2"X3/4" 49.0 40.3 6.35 5.54 27.4 20.7 4.90 4.27 44.5 12.5 12.5  
1 1/2"X1 49.0 40.3 6.35 5.54 34.1 26.4 5.69 4.98 44.5 12.5 12.5  
*NOTE :
1. Dimension Per ASME B16.11
2. Process : Hot Forming
3. Heat Treatment : Annealing After Hot Forming
4. Temp & Hold Time : 750℃±50℃, 30Min / Inch(THK)